Two-component flexible potting epoxy adhesive TET-1110
○ Can be cured at room temperature or by heating
○ Two-component formulation with excellent flowability
○ Superior crack resistance and cushioning protection
○ No cracking after 500 hours at 80°C
Typical Applications:
Battery module potting, high-voltage power supply potting,
transformer potting
| Product performance | Color | Viscosity | Curing Type Components | Component | Surface Drying Time @25℃ | Mass Ratio or Volume Ratio | Density After Mixing | Hardness | Hardness Shear Strength (Al-AI) | Thermal Conductivity | Flame retardant rating | Volume resistivity | RoHS Standard |
| Unit | / | CPS,25℃ | / | / | min | A:B | g/cm³ | ShoreA | Mpa | W/(m ·K) | Ω ·cm | Yes or No | |
| Test method | Judging by appearance | GB/T2794 | / | / | / | A:B | ASTM D792 | ASTM D2240 | GB/ T7124 | ASTM D5470 | UL94 | GB/T 1410-2006 | / |
| TET-1001 | A:Black B:Transparent | A:1031 B:307 | Room Temperature /Heating | 2K | 5~10 | 1:01 | 0.9±0.2 | 65 | 4 | / | V-0 | / | Yes |
| TET1110T | A:Transparent B:Transparent | A:27000 B:16000 | 2K | 10~15 | 1:01 | 0.9±0.2 | 80 | 17 | / | V-0 | ≥10⁴ | Yes | |
| TET1250 | A:Yellow B:Blue | A:50000 B:63000 | 2K | 20～15 | 1:01 | 0.9±0.2 | 60 | 20 | / | V-0 | ≥10 ¹ | Yes | |
| TET1215H | A:Yellow B:Blue | A:77000 B:83000 | 2K | 20～15 | 1:01 | 0.9±0.2 | 65 | 15 | 1.5 | V-0 | ≥10 ¹ | Yes | |
| TET1220H | A:Yellow B:Blue | A:87000 B:56000 | 2K | 20～15 | 1:01 | 0.9±0.2 | 70 | 12 | 2 | V-0 | ≥10 ⁴ | Yes |